NANOCRYSTALLINE sintered body based on the alpha-aluminum oxide, processes for their manufacture, and application
NANOCRYSTALLINE sintered body based on the alpha-aluminum oxide, processes for their manufacture, and application
展开▼
机译:基于α-氧化铝的NANOCRYSTALLINE烧结体,其制造方法和应用
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: metallurgy.;SUBSTANCE: sintered body contains 95-100 wt % of Al2O3, has relative density ≥97%, Vickers hardness HV0.2≥17.2 GPa and crystal structure with average dimension of primary crystals Al2O3 100 nm. A sintered body is fabricated by compacting nano-crystal powder α-Al2O3 with average diametre of particles ≤100 nm produced out of base aluminium tri-chloride with chemical formula Al2(OH)nClz, also n is a number between 2.5 and 5.5, z is number between 3.5 and 0.5, and sum n+z is constantly equal to 6, producing compaction of ≥60% density and sintering at 1200-1500°C.;EFFECT: produced abrasive grains facilitate increased efficiency of grinding.;30 cl, 3 dwg, 2 tbl, 6 ex
展开▼
机译:领域:冶金;物质:烧结体中含有95-100 wt%的Al 2 Sub> O 3 Sub>,相对密度≥97%,维氏硬度HV 0.2 < /Sub>≥17.2GPa,且晶体结构的平均晶体尺寸为Al 2 Sub> O 3 Sub> <100 nm。通过压缩由化学式为基础的三氯化铝制得的平均粒径≤100nm的纳米晶体粉末α-Al 2 Sub> O 3 Sub>制成烧结体Al 2 Sub>(OH) n Sub> Cl z Sub>,也n是2.5到5.5之间的数字,z是3.5到0.5之间的数字,和n + z始终等于6,产生≥60%的压实度,并在1200-1500°C下烧结。效果:产生的磨粒有助于提高磨削效率。; 30 cl,3 dwg,2 tbl,6 ex
展开▼