INTERNAL HIGH HARDNESS TYPE PEARLITIC RAIL WITH EXCELLENT WEAR RESISTANCE, ROLLING CONTACT FATIGUE RESISTANCE, AND DELAYED FRACTURE PROPERTY AND METHOD FOR PRODUCING SAME

摘要

An internal high hardness type pearlitic rail has a composition containing 0.73% to 0.85% by mass C, 0.5% to 0.75% by mass Si, 0.3% to 1.0% by mass Mn, 0.035% by mass or less P, 0.0005% to 0.012% by mass S, 0.2% to 1.3% by mass Cr, 0.005% to 0.12% by mass V, 0.0015% to 0.0060% by mass N, and the balance being Fe and incidental impurities, wherein the value of [% Mn]/[% Cr] is greater than or equal to 0.3 and less than 1.0, where [% Mn] represents the Mn content, and [% Cr] represents the Cr content, and the value of [% V]/[% N] is in the range of 8.0 to 30.0, where [% V] represents the V content, and [% N] represents the N content, and wherein the internal hardness of a rail head is defined by the Vickers hardness of a portion located from a surface layer of the rail head to a depth of at least 25 mm and is greater than or equal to 380 Hv and less than 480 Hv.