The black sheet and its production mannered null mass which is superior in normal temperature resistance to aging and
The black sheet and its production mannered null mass which is superior in normal temperature resistance to aging and
展开▼
机译：该黑片及其生产方式的零质量在常温下对老化和
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a thin cold-rolled steel sheet excellent in ordinary temperature delayed aging property and baking hardenability.;SOLUTION: To the thin steel sheet composed by mass% of 0.0001-0.2% C, 0.0001-0.2% N, 0.002-0.3% C + N, 0.01-3% Mn, 0.001-2% Si, 0.001-0.1% P, ≤ 0.05% S, 0.0001-0.1% Al and the balance Fe with inevitable impurities, after introducing a dislocation having 1 × 109 to 2 × 1010 cm-2 density, the aging is applied to the steel sheet and successively, the objective steel sheet is produced by newly introducing the dislocation having 1 × 109 to 2 × 1010 cm-2 density.;COPYRIGHT: (C)2005,JPO&NCIPI
展开▼
机译：解决的问题：提供一种在常温下的时效性和烘烤硬化性优异的薄冷轧钢板。解决方案：对于质量％为0.0001〜0.2％C，0.0001〜0.2％N的薄钢板， 0.002-0.3％C + N，0.01-3％Mn，0.001-2％Si，0.001-0.1％P，＆le;在引入1倍的位错之后，将0.05％的S，0.0001-0.1％的Al和余量的Fe不可避免地引入杂质中。 10 9 到2＆times;在密度为10 10 cm -2 的情况下，对钢板进行时效处理，依次引入1倍以上的位错，从而制造出目标钢板。 10 9 到2＆times; 10 10 cm -2 密度。;版权：（C）2005，JPO＆NCIPI
展开▼