Method of preparing a cellulose ester solution, method for producing a cellulose ester film and cellulose ester granulated particles
Method of preparing a cellulose ester solution, method for producing a cellulose ester film and cellulose ester granulated particles
展开▼
机译:制备纤维素酯溶液的方法,制备纤维素酯膜的方法和纤维素酯造粒的颗粒
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a method for manufacturing a cellulose ester film which has a less optical drawback even if a non-chlorine solvent is used.;SOLUTION: A preparation method of a cellulose ester solution, a manufacturing method of a cellulose ester film and a cellulose ester film comprise dissolving cellulose ester particles having: an angle of repose of not less than 20° to not more than 45°; bulk density of not less than 0.35 g/cm3 to not more than 0.75 g/cm3, tap density of not less than 0.40 g/cm3 to not more than 0.80 g/cm3, condensation of not less than 4% to not more than 20%; a particle size of 1 to 20 mm; and a 2-4C acyl group, in an organic solvent.;COPYRIGHT: (C)2002,JPO
展开▼
机译:解决的问题:提供一种即使使用非氯溶剂也具有较少光学缺陷的纤维素酯膜的制造方法。解决方案:纤维素酯溶液的制备方法,纤维素酯的制备方法膜和纤维素酯膜包括溶解的纤维素酯颗粒,所述纤维素酯颗粒的休止角不小于20°。不超过45°;堆积密度不小于0.35 g / cm3至不大于0.75 g / cm3,振实密度不小于0.40 g / cm3至不大于0.80 g / cm3,冷凝度不小于4%至不大于20 %;粒度为1至20mm;有机溶剂中的2-4C酰基。;版权所有:(C)2002,JPO
展开▼