POLYPROPYLENE PLASTIC MATERIAL OBTAINED VIA BLOW EXTRUSION, PROPYLENE FIBRE AND NONWOVEN MATERIAL FROM SAID FIBRE, AS WELL AS PRODUCTION METHODS THEREOF
POLYPROPYLENE PLASTIC MATERIAL OBTAINED VIA BLOW EXTRUSION, PROPYLENE FIBRE AND NONWOVEN MATERIAL FROM SAID FIBRE, AS WELL AS PRODUCTION METHODS THEREOF
展开▼
机译:通过吹气挤出获得的聚丙烯塑料,丙烯纤维和赛德纤维的非织造材料及其生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: chemistry.;SUBSTANCE: described is a propylene homopolymer capable of blow extrusion from molten mass. Melt flow rate ranges from 300 to 2500 g/10 minutes at 230°C. Polydispersion index ranges from 1.3 to 2.9. Melting point is equal to 160°C. The invention also describes a method of producing fibre from a propylene homopolymer, involving reaction of a metallocene compound (I), an optional organoaluminium compound and a propylene monomer The invention also describes fibre, nonwoven material and multilayer nonwoven material from the propylene homopolymer.;EFFECT: obtaining a polymer with high melt flow rate and narrow molecular weight distribution, high melting point and low content of by-products in the melt.;12 cl, 5 dwg, 4 tbl, 6 ex
展开▼
机译:领域:化学物质:描述了一种能够从熔融物料中吹塑挤出的丙烯均聚物。熔体流动速率在230°C下为300至2500 g / 10分钟。多分散指数为1.3至2.9。熔点等于160℃。本发明还描述了一种由丙烯均聚物生产纤维的方法,该方法涉及茂金属化合物(I),任选的有机铝化合物和丙烯单体的反应。本发明还描述了由丙烯均聚物制成的纤维,非织造材料和多层非织造材料。效果:获得具有高熔体流动速率和窄分子量分布,高熔点的聚合物熔体中副产物含量低。; 12 cl,5 dwg,4 tbl,6 ex