A combination of a casting process and alloy compositions that result in castings with superior combination of slow creep properties of high temperature, ductility and corrosion performance
A combination of a casting process and alloy compositions that result in castings with superior combination of slow creep properties of high temperature, ductility and corrosion performance
展开▼
机译:铸造工艺与合金成分的结合,使铸件具有高温,延展性和腐蚀性能的慢蠕变特性的优异结合
展开▼
页面导航
摘要
著录项
相似文献
摘要
A process for melting a magnesium alloy consisting of 2.0 - 6.00% by weight of aluminum, 3.00 - 8.00% by weight of rare earth metals (RE metals), the ratio between the amount being of RE metals and the amount of aluminum expressed as% by weight greater than 0.8, at least 40% by weight of RE cerium metals, less than 0.5% by weight manganese, less than 1.00% in weight of zinc, less than 0.01% by weight of calcium, less than 0.01% by weight of strontium, and the rest being magnesium and impurities unavoidable, the total impurity level being below 0.1% by weight , in which - the alloy melts into a die whose temperature is controlled in the range of 180-340 ° C, - the die is filled in a time that, expressed in milliseconds, is equal to the product of a number between 5 and 500 multiplied by the thickness of the middle part expressed in millimeters, - the static pressures of the metal are maintained during casting between 20-70 MPa and subsequently intensified until 180 MPa
展开▼