COLOR CONCRETE COMPOSITION CAPABLE OF MAINTAINING THE COLOR OF THE COMPOSITION IN CASE OF THE DAMAGE OF ROAD SURFACES AND BEING SUBSTANTIALLY APPLICABLE FOR THE EXCLUSIVE ROADS OF HIGHWAYS
COLOR CONCRETE COMPOSITION CAPABLE OF MAINTAINING THE COLOR OF THE COMPOSITION IN CASE OF THE DAMAGE OF ROAD SURFACES AND BEING SUBSTANTIALLY APPLICABLE FOR THE EXCLUSIVE ROADS OF HIGHWAYS
PURPOSE: A color concrete composition is provided to apply vivid color to concrete and secure the early strength of the concrete by adequately including type III cement, anhydrous gypsum, calcium nitrate, and pigments.;CONSTITUTION: A color concrete composition includes a binder and pigments. The binder includes 400-470 kg/m^3 of type III cement, 5-15 kg/m^3 of anhydrous gypsum, and 5-15 kg/m^3 of calcium nitrate. The ratio of water to cement(W/C) is 30-40 parts by weight. A fine aggregate rate(S/a) is 40-50 parts by weight. 0.1-1.5 part by weight of a high performance water reducing gent is included based on the binder. The amount of the fine aggregate(S) is between 700 and 900kg/m^3. The amount of coarse aggregate is between 800 and 1000kg/m^3.;COPYRIGHT KIPO 2012
展开▼
机译：用途：提供一种彩色混凝土组合物，通过适当地添加III型水泥，无水石膏，硝酸钙和颜料，为混凝土提供鲜艳的色彩并确保混凝土的早期强度。组成：一种彩色混凝土组合物，包括一种粘结剂和颜料。粘合剂包括400-470kg / m 2的III型水泥，5-15kg / m 2的无水石膏和5-15kg / m 2的硝酸钙。水与水泥的比例（W / C）为30-40重量份。细骨料比率（S / a）为40-50重量份。基于粘合剂，包括0.1-1.5重量份的高性能减水剂。细骨料的量为700至900kg / m ^ 3。粗骨料的量在800至1000kg / m ^ 3之间; COPYRIGHT KIPO 2012
展开▼