highly crystalline silver powder and a method of manufacturing the same
highly crystalline silver powder and a method of manufacturing the same
展开▼
机译:高结晶性银粉及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
fine , and good dispersion , particle size ( ) was relatively wide distribution is not too sharp , the highly crystalline silver powder crystallite is greater , and an object thereof is to provide a method of manufacturing the same . In order to achieve this object , silver nitrate , a dispersing agent and a first aqueous solution containing nitric acid , the production method of the highly crystalline silver powder comprising a step of mixing a second aqueous solution containing ascorbic acid . The dispersant is preferably a polyvinylpyrrolidone or gelatin . The highly crystalline silver powder produced by the above method . The crystallite diameter of more than 300, the mean particle diameter D 50 is 0.5 ~ 10 , the heat shrinkage rate in the longitudinal direction at 700 within 3% of the highly crystalline silver powder . The silver powder is , D 90 / D 10 is preferably a 2.1 ~ 5.0.
展开▼
机译:细且分散性好,粒度()相对较宽的分布不太尖锐,高结晶度的银粉微晶较大,其目的是提供一种制造相同的方法。为了实现该目的,硝酸银,分散剂和包含硝酸的第一水溶液,高结晶性银粉的制造方法包括将包含抗坏血酸的第二水溶液混合的步骤。分散剂优选是聚乙烯吡咯烷酮或明胶。通过上述方法生产的高结晶度银粉。微晶直径大于300,平均粒径D 50 Sub>为0.5〜10,纵向热收缩率为700%,处于高结晶性银粉的3%之内。银粉为,D 90 Sub> / D 10 Sub>优选为2.1〜5.0。
展开▼