BARIUM TITANATE DIELECTRIC POWDER, METHOD FOR MANUFACTURING THE SAME, METHOD FOR MANUFACTURING CERAMIC GREEN SHEET, AND METHOD FOR MANUFACTURING LAMINATED CERAMIC CAPACITOR
BARIUM TITANATE DIELECTRIC POWDER, METHOD FOR MANUFACTURING THE SAME, METHOD FOR MANUFACTURING CERAMIC GREEN SHEET, AND METHOD FOR MANUFACTURING LAMINATED CERAMIC CAPACITOR
展开▼
机译:钛酸钡介电粉末,其制造方法,陶瓷生片的制造方法以及叠层陶瓷电容器的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
As the temperature characteristic of the dielectric planarization, the reliability of the high electric field at high temperature to form a dielectric ceramic excellent as barium titanate based dielectric material powder, and the like to provide a method of manufacturing the same. Configure covered by the BaTiO 3 surface of the powder BaC0 3 BaCO the ratio of the BaO in a molar ratio 3 /BaO=0.55 or more of barium shall be. BaTiO to prepare a 3 powder, BaTiO 3 powder more than 16 hours, and immersed in an aqueous solvent. BaTiO 3 powder as the characteristic adjustment of the additional component added BaTiO uses 3 powder. Preparing a barium titanate based dielectric material powder and a binder, the sheet-forming slurry containing a dispersion medium of the present invention, by forming the slurry into a sheet and a ceramic green sheet. ; 展开▼