BASIC RESOURCE RESISTANT AFTER HARDENING, OBTAINED FROM COLD SELF-POLYMERIZING OR POLYMERIZING COMPOSITIONS. From a self-curing or cold-curing composition containing (A) a liquid monomeric component, (B) a pulverized component, (C) at least one initiator or initiator system for cold self-curing or polymerization, wherein in ( A) and / or (B) are / are present at least one member of the groups of aliphatic urethane acrylates and aliphatic urethane methacrylates gives a basic breakage prosthetic material, which especially after hardening has a breaking strength of 1.8 MPA * m ^ 1/2 ^ and a tensile energy absorption of 400 J / m ^ 2 ^ and preferably after 8 weeks of storage in deionized water at 50 ° C presents a difference in the yellow value of the b value of a maximum of one unit. Preferably, the elastic synthetic rubber is not present.
展开▼
机译:硬化后的基本资源抗性,可从冷自聚合或聚合组合物中获得。由自固化或冷固化的组合物组成,所述组合物包含(A)液体单体组分,(B)粉状组分,(C)至少一种用于冷自固化或聚合的引发剂或引发剂体系,其中至少存在脂族氨基甲酸酯丙烯酸酯和脂族氨基甲酸酯甲基丙烯酸酯基团中的一种,可提供基本的断裂修复材料,尤其是在硬化后,其断裂强度> 1.8 MPA * m ^ 1/2 ^拉伸能量吸收> 400 J / m ^ 2 ^,并且最好在50°C的去离子水中存储8周后,b值的黄色值之差最大为一个单位。优选地,不存在弹性合成橡胶。
展开▼