METHOD OF PRODUCING LOW PHOSPHORUS STEEL IN LD VESSELS ON OPTIMIZED MAINTENANCE OF END BLOW CARBON RANGE
METHOD OF PRODUCING LOW PHOSPHORUS STEEL IN LD VESSELS ON OPTIMIZED MAINTENANCE OF END BLOW CARBON RANGE
展开▼
机译:LD容器中低磷钢的生产及其对端吹碳范围的优化维护的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a method of consistently and reliably producing a low phosphorus steel (P 0.010%) in LD vessel by optimized maintenance of end blow carbon range (0.005-0.030%) comprising the step of charging high phosphorus containing hot liquid metal of in wt% C- 4.3-4.4, Si- 0.4-1,P- 0.100-0.300 including other normal constituents (like Ti and S) and rest iron in a LD vessel of MgO lining converting the hot liquid metal to steel by a single blowing of high purity oxygen jet along with few additives like lime, iron ore at a temperature range of 1670-1710°C and maintaining end blow carbon (final carbon in the steel after blowing) in the range of 0.03 to 0.05% to obtain final steel with low phosphorus as low as 0.010% in a single shot.
展开▼