TEMPERING METHOD OF STEEL, DIE STEEL AND METHOD FOR MANUFACTURING THE DIE STEEL USING THE TEMPERING METHOD
TEMPERING METHOD OF STEEL, DIE STEEL AND METHOD FOR MANUFACTURING THE DIE STEEL USING THE TEMPERING METHOD
展开▼
机译:钢,模具钢的回火方法以及使用该方法制造模具钢的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Disclosed is a tempering method of steel, a mold steel using the same, and a method of manufacturing the same, which can predict hardness after tempering of a steel for a mold and can also predict tempering conditions having a target hardness in manufacturing a steel for a mold. Tempering method of the steel according to the present invention is characterized in that the tempering (Tempering) the steel, it is characterized by adjusting the tempering holding temperature and holding time to have a Rockwell hardness after tempering according to the following equation (1) and (2). [Equation 1] X 1 = T (20 + Log 10 t) / 1000 " (2) " H = -1.6397 X 1 + 56.455 (X 1 17) H = -4.9419 X 1 + 114.79 (X 1 ≥ 17) (T is the tempering holding temperature (K), t is the tempering holding time (hour), H is the Rockwell hardness (HRC) after tempering)
展开▼
机译:公开了一种钢的回火方法,使用该钢的模具钢及其制造方法,其可以预测用于模具的钢的回火之后的硬度,并且还可以预测具有用于制造用于钢的模具钢的目标硬度的回火条件。一个模具。根据本发明的钢的回火方法的特征在于,对钢进行回火(Tempering),其特征在于,根据以下等式(1)调节回火保持温度和保持时间,以使回火后具有洛氏硬度。 (2)。 [等式1] X 1 Sub> = T(20 + Log 10 Sub> t)/ 1000“(2)” H = -1.6397 X 1 Sub> + 56.455(X 1 Sub> <17)H = -4.9419 X 1 Sub> + 114.79(X 1 Sub>≥17)(T是回火保持温度( K),t是回火保持时间(小时),H是回火后的洛氏硬度(HRC))
展开▼