LINE PIPE STEEL WITH EXCELLENT HIC RESISTANCE AND METHOD OF MANUFACTURING THE LINE PIPE STEEL
LINE PIPE STEEL WITH EXCELLENT HIC RESISTANCE AND METHOD OF MANUFACTURING THE LINE PIPE STEEL
展开▼
机译:具有优异抗HIC性能的管线钢及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Disclosed are a steel plate for a line pipe having excellent hydrogen induced crack resistance with a tensile strength of 450 MPa or more, and a preparation method thereof. According to the present invention, the steel plate for a line pipe, having excellent hydrogen induced crack resistance comprises: 0.03ˆ¼0.05 wt% of carbon (C); 0.2-0.3 wt% of silicon (Si); 0.5-1.3 wt% of manganese (Mn); 0.010 wt% or less of phosphorus (P); 0.005 wt% or less of sulfur (S); 0.02-0.05 wt% of aluminum (Al); 0.2-0.5 wt% of nickel (Ni); 0.2-0.3 wt% of chromium (Cr); 0.03-0.05 wt% of niobium (Nb); 0.02-0.05 wt% of vanadium (V); 0.01-0.02 wt% of titanium (Ti); 0.001-0.004 wt% of calcium (Ca); and a balance of iron (Fe) and inevitable impurities, and has a tensile strength of 450 MPa or more.