METHOD FOR PRODUCING NON-HEAT-TREATED HIGH TENSILE STRENGTH STEEL PLATE EXCELLENT IN HIGH INPUT WELDING CHARACTERISTIC AND DUCTILITY
METHOD FOR PRODUCING NON-HEAT-TREATED HIGH TENSILE STRENGTH STEEL PLATE EXCELLENT IN HIGH INPUT WELDING CHARACTERISTIC AND DUCTILITY
展开▼
机译:高输入量焊接特性和延性中非热处理高抗拉强度钢板的生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a production method capable of stably obtaining a non-heat-treated high tensile strength steel plate provided with excellent toughness in a high heat input weld heat affected zone at which weld heat input reaches 200 kJ/cm or higher and excellent base material ductility (19% or higher of total elongation) and having a plate thickness of 50 mm or lower, and in which the yield strength of the base material is 460 MPa or higher.;SOLUTION: A steel stock having a specified componential composition is heated at 1,050 to 1,200°C, is subjected to hot rolling at a cumulative draft of 30% or higher in the temperature range of 900°C or lower and at a rolling finishing temperature of an Ar3 transformation point or higher, and is cooled at a cooling velocity of 2°C/s or higher to (an Ar3 transformation point-100°C) or lower, thereafter, the cooling is stopped, and the same is reciprocated to the temperature range of an AC1 transformation point to an Ac3 transformation point, is again cooled to below 450°C at a cooling velocity of 2°C/s or higher, and is subsequently air-cooled.;COPYRIGHT: (C)2016,JPO&INPIT
展开▼