An improved method of spheroidize annealing of ypereutectoid steel wires with reduced cycle time
An improved method of spheroidize annealing of ypereutectoid steel wires with reduced cycle time
展开▼
机译:缩短循环时间的类共析钢丝球化退火的改进方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to an improved method of spheroidize annealing of hypereutectoid steel wires with reduced cycle time, comprising the steps of providing at least a standard length of hypereutectoid steel wire having about 0.6 to 0.8% of carbon in a heating furnace; directly heating the steel wire in the furnace to a temperature range of about 675°C by maintaining a heating rate substantially equal to 1.4°C/minute, the total heating time being five hours; soaking the heated steel wire within the furnace at the temperature of about 675°C for a time period of around 6.0 hours; and switching off the furnace.