Method of adding the mold flux to the continuous casting in the mold
Method of adding the mold flux to the continuous casting in the mold
展开▼
机译:在结晶器内的连铸中添加保护渣的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To prevent the occurrence of a defect by mold flux.;SOLUTION: The mold flux having bulk specific gravity of 1.2 g/cm3 or less is added in a casting mold 2. Here, a falling distance (an addition height) H up to a non-molten layer from a falling starting position for making the mold flux free fall is set to 250 mm or less when adding the mold flux in a state where a thickness of the non-molten layer 22 in the casting mold 2 becomes 20 mm or more and a thickness of a molten layer 23 becomes 10 mm or more. The flux falling zone area A when adding the mold flux is also set to 0.0025 m2 or more, and a supply speed Q of the mold flux in a falling zone is set to 1760 kg/(m2.min.) or less.;COPYRIGHT: (C)2014,JPO&INPIT
展开▼
机译:解决的问题:为了防止由铸模助焊剂引起的缺陷的产生。;解决方案:将体积比重为1.2 g / cm 3 Sup>或更小的铸模助焊剂添加到铸模2中。另外,在以非熔融金属的厚度的状态添加脱模剂的情况下,从使脱模剂自由落下的脱模开始位置起直至非熔融层为止的脱模距离(附加高度)H为250mm以下。铸模2中的熔融层22变为20mm以上,熔融层23的厚度变为10mm以上。添加铸模助焊剂时的助焊剂落下区域面积A也设为0.0025m 2 Sup>以上,落模中的助焊剂的供给速度Q设为1760kg /(m < Sup> 2 Sup> .min。)或更少。; COPYRIGHT:(C)2014,JPO&INPIT
展开▼