GRAY CAST IRON FOR CYLINDER LINER AND METHOD FOR MANUFACTURING CYLINDER LINER USING THE SAME
GRAY CAST IRON FOR CYLINDER LINER AND METHOD FOR MANUFACTURING CYLINDER LINER USING THE SAME
展开▼
机译:汽缸套用灰铸铁及其制造汽缸套的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A gray cast iron for a cylinder liner is provided that maintains fatigue strength and thermal shock property by adjusting component contents. The gray cast iron includes carbon (C) in an amount of about 3.2 to 3.7 weight % (wt %); silicon (Si) in an amount of about 2.0 to 2.8 wt %; manganese (Mn) in an amount of about 0.50 to 1.0 wt %; phosphorus (P) in an amount of about 0.20 wt % or less, and greater than about 0 wt %; sulfur (S) in an amount of about 0.10 wt % or less, and greater than about 0 wt %; chromium (Cr) in an amount of about 0.50 wt % or less, and greater than about 0 wt %; copper (Cu) in an amount of about 0.20 to 0.80 wt %; molybdenum (Mo) in an amount of about 0.10 to 0.40 wt %; and the balance of iron (Fe), based on the total weight of the gray cast iron.