ALUMINA-ZIRCONIA-SILICA FUSED-CAST REFRACTORY MATERIAL, GLASS FURNACE, AND METHOD FOR PRODUCING SHEET GLASS
ALUMINA-ZIRCONIA-SILICA FUSED-CAST REFRACTORY MATERIAL, GLASS FURNACE, AND METHOD FOR PRODUCING SHEET GLASS
展开▼
机译:铝-氧化锆-二氧化硅熔铸耐火材料,玻璃熔炉以及制备玻璃板的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Provided are: an alumina-zirconia-silica fused-cast refractory material suitable as a refractory material for glass production apparatuses, and which suppresses the exudation of glass components from the refractory material; and a glass furnace using same. An alumina-zirconia-silica fused-cast refractory material containing, as essential components, Al2O3, ZrO2, SiO2 and Na2O, in mass percentage in oxide equivalent, 20.0% ≤ Al2O3 ≤ 70.0%, 10.0% ≤ ZrO2 41.5%, 3.8% ≤ SiO2 ≤ 18.0%, 1.3% ≤ Na2O ≤ 15.0%, where Al2O3/SiO2 6.5, 0.20 ≤ Na2O/SiO2, and the total amount of the abovementioned essential components is at least 85%.