Fused-cast alumina-zirconia-silica refractory and glass melting furnace employing it
Fused-cast alumina-zirconia-silica refractory and glass melting furnace employing it
展开▼
机译:熔融铸造的氧化铝-氧化锆-二氧化硅耐火材料和玻璃熔炼炉
展开▼
页面导航
摘要
著录项
相似文献
摘要
A fused-cast-alumina-zirconia-silica refractory consisting essentially of corundum crystals, baddeleyite crystals and a matrix glass phase and having a chemical composition comprising (a) from 30 to 70 wt% of Al2O3, (b) from 20 to 59 wt% of ZrO2, (c) from 5 to 12 wt% of SiO2, (d) from 0.15 to 0.60 wt% of Na2O, (e) from 0 to 0.50 wt% of K2O, (f) from 0 to 0.40 wt% of Li2O, (g) from 0.05 to 0.80 wt% of B2O3, (h) from 0.05 to 0.80 wt% of P2O5, and (i) from 0.05 to 0.50 wt% in total of at least one member selected from the group consisting of SnO2, ZnO, CuO and MnO2.
展开▼
机译:一种基本上由刚玉晶体,坏钙铁矿晶体和基质玻璃相组成的熔铸氧化铝-氧化锆-硅质耐火材料,其化学成分包括(a)30至70 wt%的Al 2 Sub> O 3 Sub>,(b)ZrO 2 Sub>的20至59 wt%,(c)SiO 2 Sub>的5至12 wt%,( d)Na 2 Sub> O的0.15至0.60 wt%,(e)K 2 Sub> O的0至0.50 wt%,(f)0至0.40 wt% Li 2 Sub> O的含量,(g)为B 2 Sub> O 3 Sub>的重量百分比,(h)0.05至0.80重量% P 2 Sub> O 5 Sub>,和(i)总计0.05至0.50 wt%的至少一种选自SnO 2 Sub>,ZnO,CuO和MnO 2 Sub>。
展开▼