OPAQUE FLUOROPOLYMER COMPOSITION COMPRISING WHITE PIGMENTS FOR PHOTOVOLTAIC ELEMENTS OF SOLAR CELLS
OPAQUE FLUOROPOLYMER COMPOSITION COMPRISING WHITE PIGMENTS FOR PHOTOVOLTAIC ELEMENTS OF SOLAR CELLS
展开▼
机译:包含白色颜料的不透明含氟聚合物组合物,用于太阳能电池的光伏元素
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a fluoropolymer composition having a total light transmittance (TT) of less than 15% as measured according to ASTM D1003 on a sample having a thickness of about 50 μm, said composition comprising: - at least one hydrogen- (Polymer (A)); - from 5 to 80% by weight, based on the polymer (A), of at least one inorganic pigment [pigment (I)]; And tetrafluoroethylene (TFE) copolymers having a dynamic viscosity of less than 100 Pa x sec at a temperature of 280 DEG C and a shear rate of 1 radx sec -1 % Of per (halo) fluoropolymer [polymer (B)]. The addition of the polymer (B) to the composition based on the polymer (A) advantageously allows the pigment (I) to be dispersed uniformly, resulting in a composition which can still be processed in the form of a film while retaining excellent opacity, A film providing properties can be manufactured.
展开▼
机译:本发明涉及一种氟聚合物组合物,其根据ASTM D1003在厚度约为50μm的样品上的总透光率(TT)小于15%,所述组合物包含:-至少一种氢-(聚合物(一种)); -基于聚合物(A)为5-80重量%的至少一种无机颜料[颜料(I)];四氟乙烯(TFE)共聚物,其在(280)℃的温度下的动态粘度小于100 Pa x sec,剪切速率为每(卤)含氟聚合物的1 radx sec Sup> -1 Sup% [聚合物(B)]。将聚合物(B)添加到基于聚合物(A)的组合物中有利地使颜料(I)均匀分散,从而得到在保持优异的不透明性的情况下仍可以以膜形式加工的组合物,可以制造提供特性的膜。
展开▼