Si METHOD FOR PRODUCING HIGH SI-CONTENT AUSTENITIC STAINLESS STEEL
Si METHOD FOR PRODUCING HIGH SI-CONTENT AUSTENITIC STAINLESS STEEL
展开▼
机译:生产高Si含量奥氏体不锈钢的Si方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A high Si austenitic stainless steel which exhibits stable acid resistance and good corrosion resistance in high temperature and high concentration nitric acid is characterized by containing 0.04% or less of C, 2.5 to 7.0% of Si, 10% or less of Mn, 0.03% or less of P, % Or less, N: 0.035% or less, sol. At least one of Nb, Ti, Ta, and Zr: 0.05 to 0.7% in total; the balance: Fe and impurities , And the total amount of the B 1 inclusions measured by the method described in JIS G 0555 (2003) Annex 1 "Method of Microscopic Test of Nonmetallic inclusions by the Point Acid Method" is 0.03 area% or less.
展开▼
机译:在高温和高浓度硝酸中具有稳定的耐酸性和良好的耐腐蚀性的高Si奥氏体不锈钢的特征在于,含有0.04%以下的C,2.5%至7.0%的Si,10%以下的Mn,0.03% P:%以下; N:0.035%以下;溶胶。 Nb,Ti,Ta和Zr中的至少一种:总计0.05〜0.7%。平衡:Fe和杂质,以及通过JIS G 0555(2003)附件1“通过点酸法对非金属夹杂物进行显微测试的方法”中描述的方法测量的B 1 Sub>夹杂物的总量小于等于0.03面积%。