MESOPOROUS AND MACROPOROUS NICKEL CATALYST HAVING A MEDIAN MACROPOROUS DIAMETER OF MORE THAN 200 NM AND ITS USE IN HYDROGENATION
MESOPOROUS AND MACROPOROUS NICKEL CATALYST HAVING A MEDIAN MACROPOROUS DIAMETER OF MORE THAN 200 NM AND ITS USE IN HYDROGENATION
展开▼
机译:中微孔直径大于200海里的中,大孔镍催化剂及其在加氢中的应用
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to a supported catalyst comprising a calcined, predominantly aluminum oxide support and an active phase comprising nickel, the nickel content being between 5 and 65% by weight of said element relative to the total mass of the catalyst, said active phase not comprising no Group VIB metal, the nickel particles having a diameter of less than or equal to 20 nm, said catalyst having a mesoporous median diameter between 8 nm and 25 nm, a macroporous median diameter greater than 200 nm, a mesoporous volume measured by mercury porosimetry greater than or equal to 0.30 mL / g and a total pore volume measured by mercury porosimetry greater than or equal to 0.34 mL / g. The invention also relates to the process for preparing said catalyst and its use in a hydrogenation process.
展开▼
机译:本发明涉及一种载体催化剂,其包括煅烧的,主要为氧化铝的载体和包含镍的活性相,相对于催化剂的总质量,镍含量为所述元素的5-65重量%,所述活性相不包含不含VIB族金属,镍颗粒的直径小于或等于20 nm,所述催化剂的介孔中值直径在8 nm至25 nm之间,大孔中值直径大于200 nm,通过汞孔隙率法测得的中孔体积大于或等于0.30 mL / g,并且通过水银孔率法测得的总孔体积大于或等于0.34 mL / g。本发明还涉及制备所述催化剂的方法及其在氢化方法中的用途。
展开▼