Materials for automobiles, low cost and excellent in salt damage corrosion resistance and oil supply pipe
Materials for automobiles, low cost and excellent in salt damage corrosion resistance and oil supply pipe
展开▼
机译:用于汽车的材料,成本低,耐盐腐蚀和供油管性能优良
展开▼
页面导航
摘要
著录项
相似文献
摘要
It is an object of the present invention to provide an automobile member and an oil supply pipe which are inexpensive and excellent in corrosion resistance against salt damage. C: 0.015%, N: 0.015%, Cr: 10.5 to 18.0%, Si: 0.01 to 0.80%, Mn: 0.01 to 0.80% by mass% 80%, P 0.050%, S: 0.010%, Al: 0.010 to 0.100%, Ti: 0.03 to 0.30% and Nb: It is exposed to a salt damage environment between a member made of ferritic stainless steel containing one kind or two kinds of 03 to 0.30% as a material and a metal part molded from an Al-plated stainless steel plate attached to a member The Al plating adhesion amount of the metallic parts on the surface corresponding to the gap part of the gap structure part is 20 g / m2150 g / m2Or less, and the members other than the gap portion and the surfaces of the metal parts are covered with a cationic electrodeposition coating film having a thickness of 5 to 35 m.
展开▼
机译:本发明的目的是提供一种廉价且耐盐蚀性优异的汽车部件和供油管。 C:0.015%,N:0.015%,Cr:10.5〜18.0%,Si:0.01〜0.80%,Mn:0.01〜0.80质量%80%,P 0.050%,S:0.010%,Al:0.010〜0.100 %,Ti:0.03〜0.30%,Nb:在含有03〜0.30%的一种或两种的铁素体系不锈钢制的部件与由Al-模压成型的金属部件之间,暴露于盐分破坏环境。附着在部件上的电镀不锈钢板与间隙结构部分的间隙部分相对应的表面上的金属部分的Al镀覆附着量为20 g / m 2 Sup> 150 g / m 小于或等于2 ,并且除间隙部分和金属部件的表面以外的部件覆盖有厚度为5至35m的阳离子电沉积涂膜。
展开▼