The invention pertains to the use of a nitrogen-doped porous carbon material in a supercapacitor, wherein the nitrogen-doped porous carbon material has the following properties:- a nitrogen content in the range of 0.50 to 8.0 at% as determined via XPS- a specific surface area (N2 , BET) of at least 1000 m2/g- a total pore volume as determined by N2 adsorption of at least 0.80 ml/g,- a N2 adsorption pore size distribution which is such that at least 50% of the pore volume is in pores with a diameter of above 2 nm.;The invention further pertains to a supercapacitor, an electrode for use in a supercapacitor, to specific nitrogen-doped porous carbon materials and to methods for the manufacture thereof.
展开▼
机译:本发明涉及氮掺杂的多孔碳材料在超级电容器中的用途,其中氮掺杂的多孔碳材料具有以下特性:-通过XPS测定的氮含量为0.50至8.0 at%-比表面积(N2,BET)至少为1000 m2 / g-通过氮气吸附确定的总孔体积至少为0.80 ml / g,-N 2吸附孔径分布,使得至少50%的孔体积位于直径大于2nm的孔中。本发明还涉及超级电容器,用于超级电容器的电极,特定氮掺杂的多孔碳材料及其制造方法。
展开▼