NICKEL-ZINC-COPPER BASED FERRITE PARTICLE, RESIN COMPOSITION, AND RESIN MOLD
NICKEL-ZINC-COPPER BASED FERRITE PARTICLE, RESIN COMPOSITION, AND RESIN MOLD
展开▼
机译:基于镍-锌-铜的铁素体颗粒,树脂组成和树脂模具
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide: ferrite particles high in saturation magnetization and electric resistance, and superior in dispersibility in a resin, a solvent or a resin composition; a resin composition including the ferrite particles; and a resin mold arranged by use of the resin composition.SOLUTION: A Ni-Zn-Cu based ferrite particle comprises a single crystal material having an average particle diameter of 1-2000 nm, and has a polyhedral particle shape. The Ni-Zn-Cu based ferrite particle includes: 5-10 wt.% of Ni; 15-30 wt.% of Zn; 1-5 wt.% of Cu; and 25-50 wt.% of Fe.SELECTED DRAWING: Figure 1