Method for producing journal part of 9 to 12 Cr steel turbine rotor, and journal part produced by the method
Method for producing journal part of 9 to 12 Cr steel turbine rotor, and journal part produced by the method
展开▼
机译:9〜12%Cr钢制涡轮转子的轴颈零件的制造方法以及通过该方法制造的轴颈零件
展开▼
页面导航
摘要
著录项
相似文献
摘要
In a journal part of a 9 to 12 wt % Cr steel turbine rotor, a groove face is formed, and on the groove face, a lower build-up layer is formed by using a first welding material containing C: 0.10 to 0.25 wt %, Si: 0.20 to 0.80 wt %, Mn: 1.0 to 2.5 wt %, Ni: 0.4 to 1.0 wt %, Cr: 1.0 to 3.0 wt %, Mo: 0.2 to 1.5 wt %, V: 0.03 to 0.10 wt %, and a remainder composed of Fe and inevitable impurities, and further on this lower build-up layer, an upper build-up layer is formed using a second welding material containing C: 0.10 to 0.25 wt %, Si: 0.20 to 0.80 wt %, Mn: 1.0 to 2.5 wt %, Ni: 0.4 to 1.0 wt %, Cr: 1.0 to 3.0 wt %, Mo: 0.2 to 1.5 wt %, and a remainder consisting of Fe and inevitable impurities.