METHOD OF LIGHT-WEIGHT FOAMING ACOUSTIC ABSORBENT PANEL UASING A FLY-ASH AND THE LIGHT-WEIGHT FOAMING ACOUSTIC ABSORBENT PANEL MANUFACTURED BY THE METHOD
METHOD OF LIGHT-WEIGHT FOAMING ACOUSTIC ABSORBENT PANEL UASING A FLY-ASH AND THE LIGHT-WEIGHT FOAMING ACOUSTIC ABSORBENT PANEL MANUFACTURED BY THE METHOD
展开▼
机译:粉煤灰的轻质泡沫吸音板的制造方法及该方法制得的轻质泡沫吸音板
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a lightweight foamed sound absorption panel manufacturing method using fly ash and a lightweight foamed sound absorption panel manufactured by the same and, more specifically, to a lightweight foamed sound absorption panel manufacturing method using fly ash and a lightweight foamed sound absorption panel manufactured by the same capable of improving flexural strength, water repellency, a sound absorption function, deodorization, and an antibacterial ability without a whitening phenomenon. The present invention relates to a composite comprising: 4 to 8 parts by weight of an alkaline water-containing oxide; 1 to 5 parts by weight of an acid; 1 to 5 parts by weight of a strength reinforcing material; and 1 to 10 parts by weight of water for 100 parts by weight of a mixture having 50 to 80 wt% of the fly ash and 20 to 50 wt% of an alkali silicate. The lightweight foamed sound absorption panel manufacturing method using the fly ash comprises: a composite mixing and injecting step of mixing the composite during 5-10 minutes, and injecting the mixed composite into a mold; a moisture deodorizing and foaming step of instantly heating the mold at 100C within 8-10 seconds, and heating the same for 8-12 minutes to remove moisture and perform foaming after the composite mixing and injecting step; a curing step of heating the mold in an oven at 300C during 1-3 hours after the moisture deodorizing and foaming step, and manufacturing the lightweight foamed sound absorption panel; and a cutting step of cutting the lightweight foamed sound absorption panel manufactured through the curing step depending on a use purpose.
展开▼