A high-intensity and high-modulus glass fiber is provided. Said fiber is produced by improving the processes, components and proportion of conventional E-glass production process and apparatus. The fiber contains 13% CaO at most, no boron and fluorine, meanwhile ZrO 2 and Li 2 O is first added, B 2 O 3 is first removed, and SO 3 is added. The intensity and the modulus of the fiber are slightly lower than those of S-glass or T-glass, but obviously higher than those of E-glass and ECR-glass which are highly produced and widely used or other boron-free glass such as Advantex glass. Besides the intensity, modulus and fatigue resistance, said fiber has obvious advantages over E-glass in heat, acid and alkali resistance. The glass fiber roving made from said fiber has 22% higher tensile strength and 11ˆ¼15.7% higher modulus than those of E-glass, and has 16% higher tensile strength and 5ˆ¼6% higher modulus than those of ECR-glass.
展开▼
机译:提供了一种高强度,高模量的玻璃纤维。所述纤维是通过改进常规电子玻璃生产工艺和设备的工艺,组分和比例来生产的。该纤维最多包含13%的CaO,不含硼和氟,同时首先添加ZrO 2和Li 2 O,首先去除B 2 O 3,然后添加SO 3。纤维的强度和模量略低于S玻璃或T玻璃,但明显高于高产量且广泛使用的E玻璃和ECR玻璃或其他无硼玻璃,例如Advantex玻璃。除了强度,模量和抗疲劳性外,所述纤维在耐热性,耐酸碱性方面也比电子玻璃具有明显的优势。由所述纤维制成的玻璃纤维粗纱比E-玻璃具有更高的抗张强度22%和更高的模数11-11.57.7%,并且比ECR-玻璃具有更高的16%的抗拉强度和更高的5%-6%的模量。
展开▼