摘要
PROBLEM TO BE SOLVED: To measure fluidity of high-fluidity concrete conventionally because ready-mixed concrete is used as a test body, and there is a problem that it takes time and effort. In addition, the conventional test method has a problem that the water cement of concrete is high and concrete with a low water cement ratio cannot be evaluated appropriately. SOLUTION: Standard sand specified in JIS R 5201 is blended with high-strength cement, sand cement ratio (S / C) 50 to 70% by mass, water cement ratio (W / C) 12 to 15% by mass, And for mortar in which the amount of high-performance water reducing agent added is 1 to 5% by mass of the above cement, the static flow specified in JIS R 5201 is 260 mm or more and the time required for the static flow to reach 250 mm is 30 to 60. High-strength, high-fluidity concrete is manufactured using high-strength cement in the range of seconds. [Selection diagram] Fig. 1
展开▼
机译:解决的问题:由于使用预拌混凝土作为测试体,因此常规上要测量高流动性混凝土的流动性,并且存在耗时费力的问题。另外,传统的测试方法存在以下问题:混凝土的水胶泥含量高,并且不能适当地评估具有低的水胶泥比例的混凝土。解决方案:将JIS R 5201中指定的标准砂与高强度水泥混合,砂水泥比(S / C)为50至70质量%,水水泥比(W / C)为12至15质量%,并且用于砂浆高性能减水剂的添加量为上述水泥的1〜5质量%,JIS R 5201中规定的静流为260mm以上,达到250mm的时间为30到60。高强度,高流动性的混凝土是在几秒钟内使用高强度水泥制造的。 [选择图]图1
展开▼