Method For Producing An Ausferritic Steel, Austempered During Continuous Cooling Followed By Annealing

摘要

A method for producing an austempered steel is provided. The method includes subjecting a steel alloy having a silicon content of 1.5 to 4.4 weight percent and a carbon content of 0.3 to 0.8 weight percent to continuous cooling followed by annealing. The cooling rate is initially sufficiently fast to prevent predominant formation of proeutectoid ferrite or pearlite, while subsequently at intermediate temperatures, the cooling rate is sufficiently slow to allow a transformation of the austenite to mainly ausferrite during cooling. The annealing is able to complete the transformation of carbon enriched austenite to ausferrite and to temper any martensite previously formed. The method results in the cost-efficient production of one or more continuously cooled and annealed austempered steel components or semi-finished products having mainly an ausferritic microstructure.