DIPHOSPHORUS PENTASULFIDE COMPOSITION FOR SULFIDE-BASED INORGANIC SOLID ELECTROLYTE MATERIAL
DIPHOSPHORUS PENTASULFIDE COMPOSITION FOR SULFIDE-BASED INORGANIC SOLID ELECTROLYTE MATERIAL
展开▼
机译:硫化物基无机固体电解质材料的二硫五硫化物组合物
展开▼
页面导航
摘要
著录项
相似文献
摘要
The purpose of the present invention is to provide a diphosphorus pentasulfide composition from which a sulfide-based inorganic solid electrolyte material having improved lithium ion conductivity can be obtained. The present invention pertains to a diphosphorus pentasulfide composition for a sulfide-based inorganic solid electrolyte material, the diphosphorus pentasulfide composition having a molar ratio (S/P) of 2.40-2.49 which is the content of sulfur (S) to the content of phosphorus (P), wherein in a DSC curve of the diphosphorus pentasulfide composition, obtained by measurement using a differential scanning calorimeter under the conditions of a starting temperature of 25°C, a measurement temperature in the range of 30-350°C, a heating rate of 5°C/min, and an argon atmosphere of 100 ml/min, the DSC curve has an endothermic peak in the temperature range of 280-300°C, and the full width at half maximum of the endothermic peak is at least 4.1°C.
展开▼
机译:本发明的目的是提供一种五硫化二磷组合物,从其可以得到具有改善的锂离子传导性的基于硫化物的无机固体电解质材料。本发明涉及一种用于基于硫化物的无机固体电解质材料的五硫化二磷组合物,该五硫化二磷组合物的摩尔比(S / P)为2.40-2.49,这是硫含量(S)与磷含量的比值。 (P),其中在起始温度为25℃的条件下通过使用差示扫描量热计的测量获得的五硫化二磷组合物的DSC曲线中,测量温度为30-350℃,在5°C / min的速率和100 ml / min的氩气气氛下,DSC曲线在280-300°C的温度范围内具有吸热峰,且吸热峰的半峰全宽至少为4.1℃。
展开▼