Welding materials for austenitic heat-resistant steels, weld metals and welded structures, and methods of making weld metals and welded structures
Welding materials for austenitic heat-resistant steels, weld metals and welded structures, and methods of making weld metals and welded structures
展开▼
机译：奥氏体耐热钢，焊接金属和焊接结构的焊接材料，以及制造焊接金属和焊接结构的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Chemical composition is in mass%, C: 0.06 to 0.14%, Si: 0.10 to 0.40%, Mn: 2.0 to 4.0%, P: 0.020% or less, Cu: 2.0 to 4.0%, Ni: 15.0 to 19.0%, Cr ： 16.0 ~ 20.0%, Mo ： 0.50 ~ 1.50%, Nb ： 0.30 ~ 0.60%, N ： 0.10 ~ 0.30%, Al ： 0.030% or less, O ： 0.020% or less, S ： 0 ~ 0.0030%, Sn ： 0 ~ 0.0030%, Bi: 0 to 0.0030%, Zn: 0 to 0.0030%, Sb: 0 to 0.0030%, As: 0 to 0.0030%, V: 0 to 0.50%, Ti: 0 to 0.50%, Ta: 0 to 0.50 %, Co: 0 to 2.0%, B: 0 to 0.020%, Ca: 0 to 0.020%, Mg: 0 to 0.020%, REM: 0 to 0.06%, balance: Fe and impurities, S, Sn, Bi, A welding material for austenitic heat-resistant steel, containing two or more selected from Zn, Sb and As in a range satisfying [0.0005≤S + Sn + Bi + Zn + Sb + As≤0.0030].
展开▼
机译：化学成分为质量％，C：0.06〜0.14％，Si：0.10〜0.40％，Mn：2.0〜4.0％，P：0.020％以下，Cu：2.0〜4.0％，Ni：15.0〜19.0％，Cr ：16.0〜20.0％，Mo：0.50〜1.50％，Nb：0.30〜0.60％，N：0.10〜0.30％，Al：0.030％以下，O：0.020％以下，S：0〜0.0030％，Sn： 0〜0.0030％，Bi：0至0.0030％，Zn：0至0.0030％，Sb：0至0.0030％，As：0至0.0030％，V：0至0.50％，Ti：0至0.50％，Ta：0至0.50％，Co：0至2.0％，B：0至0.020％，Ca：0至0.020％，Mg：0至0.020％，REM：0至0.06％，余量：Fe和杂质，S，Sn，Bi ，奥氏体耐热钢用焊接材料，其在满足[0.0005≤S+ Sn + Bi + Zn + Sb +As≤0.0030]的范围内含有选自Zn，Sb和As中的两种以上。
展开▼