HIGH-STRENGTH MANGANESE STEEL CONTAINING ALUMINIUM, METHOD OF PRODUCING SHEET STEEL PRODUCT FROM SAID STEEL AND SHEET STEEL PRODUCT OBTAINED ACCORDING TO SAID METHOD
HIGH-STRENGTH MANGANESE STEEL CONTAINING ALUMINIUM, METHOD OF PRODUCING SHEET STEEL PRODUCT FROM SAID STEEL AND SHEET STEEL PRODUCT OBTAINED ACCORDING TO SAID METHOD
展开▼
机译:含铝高强度锰钢的生产方法以及根据上述方法获得的普通钢材和普通钢材的生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: metallurgy.;SUBSTANCE: invention relates to metallurgy, namely to high-strength aluminum-containing manganese steel used in automotive industry, shipbuilding, aerospace industry, and so forth. Steel has the following chemical composition, wt. %: C: 0.01 to 0.3, Mn: 4 to 10, Al: 1 to 4, Si: 0.01 to 1, Cr: 0.1 to 4, Mo: 0.02 to 1, P: less than 0.1, S: less than 0.1, N: less than 0.3, optionally, at least one of: V: from 0.01 to 1, Nb: from 0.01 to 1, Ti: from 0.01 to 1, Sn: from 0 to 0.5, Cu: from 0.005 to 3, W: from 0.03 to 3, Co: from 0.05 to 3, Zr: from 0.03 to 0.5, Ca: from 0.0005 to 0.1, iron and unavoidable impurities - the rest. Steel has tensile strength Rm from 800 MPa to 1700 MPa, elongation at breaking A50 from 6 % to 45 %, preferably from 8 % to 45 %, and microstructure containing from 5 to 65 % residual austenite.;EFFECT: steel has high deformation properties, high resistance to delayed formation of cracks and hydrogen embrittlement.;14 cl
展开▼