Improved aluminide/barrier coating combinations for dispersion strengthened nickel materials were investigated. The barrier materials involved alloys with refractory metal content to limit interdiffusion between the coating and the substrate, thereby minimizing void formation. Improved aluminide coatings involved the dispersion of aluminum-rich compounds. Coatings were tested in argon at 1533 K (2300 F) for 100 hours and in cyclic oxidation at 1422 K (2100 F). Two coatings on TDNiCr completed 300 hours of oxidation testing, none on TDNi. Selected coating combinations were evaluated in Mach 1 burner rig testing using JP-4 fuel and air at 1422 K (2100 F) and 1477 K (2200 F) for 350 and 100 hours, respectively. Static oxidation in 1-hour cycles was conducted at 1533 K (2300 F) for 100 hours. For comparison purposes a physical vapor deposition (PVD) NiCrAlY coating was tested concurrently. Only the NiCrA1Y coating survived the 1477 K (2200 F)/100-hour burner rig test and 275 hours of the 350-hour 1422 K (2100 F) test. Elevated temperature exposure reduced room temperature tensile properties but had little effect on elevated temperature properties. (Author)
展开▼