Deformation Characteristics and Failure Modes of Notched Graphite Polymide Composites at Room and Elevated Temperatures

摘要

The fracture behavior in graphite/polyimide (Gr/PI) Celion 6000/PMR-15 composites was characterized. Emphasis was placed on the correlation between the observed failure modes and the deformation characteristics of center-notched Gr/Pl laminates. Crack tip damage growth, fracture strength and notch sensitivity, and the associated characterization methods were also examined. Special attention was given to nondestructive evaluation of internal damage and damage growth, techniques such as acoustic emission, X-ray radiography, and ultrasonic C-scan. Microstructural studies using scanning electron microscopy, photomicrography, and the pulsed nuclear magnetic resonance technique were employed as well. All experimental procedures and techniques are described and a summary of representative results for Gr/Pl laminates is given.