Fire Test Methodology for Aerospace Materials. 1: Thermal and Smoke Toxicological Assessments of Graphite/Bismaleimide and Graphite/Epoxy Systems

摘要

Both materials possess a high degree of thermal stability, with total heat release values being essentially identical under piloted ignition conditions over a range of 5 to 10 W/sq cm incident heat flux. The graphite/epoxy material had a tendency to auto-ignite at a lower heat flux (about 7 W/sq cm) and produced about 23 percent higher peak heat release rates, approximately 42 percent more carbon monoxide and considerably more smoke than the graphite/bismaleimide under conditions of piloted ignition. Toxicological potencies of smoke produced from the two composites were equivalent for 30 minute exposures. Potencies were also comparable to many common materials, such as wood. There was no evidence for the formation of an 'unusual toxicant' nor for any short term post-exposure toxicological effects.