Modification of Silicon Carbide Fibers for Use in SIC/Ti Composites

摘要

The degradation of silicon carbide fibers during exposure to conditions typical of composite fabrication was investigated. The tensile strength of pristine fibers and fibers sputtered with thin metal coatings were determined before and after treatment at 870 C for one hour in vacuum. Each fiber strength distribution was related by an analytical procedure to a projected composite ultimate tensile strength (PC UTS). The results indicate that a thin aluminum diffusion barrier can yield a 150 percent increase in PC UTS over the baseline SiC/Ti system.