Buckling of a Sublaminate in a Quasi-Isotropic Composite Laminate

摘要

The buckling of an elliptic delamination embedded near the surface of a thick quasi-isotropic laminate was predicted. The thickness of the delaminated ply group (the sublaminate) was assumed to be small compared to the total laminate thickness. Finite-element and Rayleigh-Ritz methods were used for the analyses. The Rayleigh-Ritz method was found to be simple, inexpensive, and accurate, except for highly anisotropic delaminated regions. Effects of delamination shape and orientation, material anisotropy, and layup on buckling strains were examined. Results show that: (1) the stress state around the delaminated region is biaxial, which may lead to buckling when the laminate is loaded in tension; (2) buckling strains for multi-directional fiber sublaminates generally are bounded by those for the 0 deg and 90 deg unidirectional sublaminates; and (3) the direction of elongation of the sublaminate that has the lowest buckling strain correlates with the delamination growth direction.