Aerothermal Performance and Damage Tolerance of a Rene 41 Metallic Standoff Thermal Protection System at Mach 6.7

摘要

A flight-weight, metallic thermal protection system (TPS) model applicable to Earth-entry and hypersonic-cruise vehicles was subjected to multiple cycles of both radiant and aerothermal heating in order to evaluate its aerothermal performance, structural integrity, and damage tolerance. The TPS was designed for a maximum operating temperature of 2060 R and featured a shingled, corrugation-stiffened corrugated-skin heat shield of Rene 41, a nickel-base alloy. The model was subjected to 10 radiant heating tests and to 3 radiant preheat/aerothermal tests. Under radiant-heating conditions with a maximum surface temperature of 2050 R, the TPS performed as designed and limited the primary structure away from the support ribs to temperatures below 780 R. During the first attempt at aerothermal exposure, a failure in the panel-holder test fixture severely damaged the model. However, two radiant preheat/aerothermal tests were made with the damaged model to test its damage tolerance. During these tests, the damaged area did not enlarge; however, the rapidly increasing structural temperature measuring during these tests indicates that had the damaged area been exposed to aerodynamic heating for the entire trajectory, an aluminum burn-through would have occurred.