Test and analysis of a stitched RFI graphite-epoxy panel with a fuel access door

摘要

A stitched RFI graphite-epoxy panel with a fuel access door was analyzed using a finite element analysis and loaded to failure in compression. The panel was initially 56-inches long and 36.75-inches wide and the oval access door was 18-inches long and 15-inches wide. The panel was impact damaged with impact energy of 100 ft-lb prior to compressive loading; however, no impact damage was detectable visually or by A-scan. The panel carried a failure load of 695,000 Ib and global failure strain of .00494 in/in. Analysis indicated the panel would fail due to collapse at a load of 688,100 Ib. The test data indicate that the maximum strain in a region near the access door was .0096 in/in and analysis indicates a local surface strain of .010 in/in at the panel's failure load. The panel did not fail through the impact damage, but instead failed through bolt holes for attachment of the access door in a region of high strain.