Effect of particle size and particle size distribution on physical characteristics, morphology and crystal structure of explosively compacted high-T(sub c) superconductors

摘要

A superconductor, of composition Y(Ba,K,Na)2Cu3O(x)/F(y) and a composite of composition Y(Ba,K,Na)2Cu3O(x)/F(y) Ag, with changing K, Na and F content but a constant silver content (Ag = 10 mass%) was prepared using a single heat treatment. the resulting material was ground in a corundum lined mill, separated to particle size fractions of 0-40 micron, 0-63 micron and 63-900 micron and explosively compacted, using an explosive pressure of 10(exp 4) MPa and a subsequent heat treatment. Best results were obtained with the 63-900 micron fraction of composition Y(Ba(1.95) K(0.01)Cu3O(x)F(0),(05)/Ag: porosity less than 0.01 cu cm/g and current density 2800 A/sq cm at 77K.