Lubricating Properties of Lead-Monoxide-Base Coatings of Various Compositions at Temperatures to 1250 F

摘要

A number of ceramic coatings of different compositions containing lead monoxide (PbO) were studied to determine their relative merits as dry-film lubricants. Lead monoxide is known to be an effective solid lubricant at elevated temperatures, and this oxide was the main component in all compositions studied. Friction and wear properties were determined at temperatures from 750 to 1250 F, at a sliding velocity of 430 feet per minute, and at a normal load of 1 kilogram. In all of the coatings, PbO was the component primarily responsible for the lubricating properties. Oxides other than PbO had an indirect effect on lubrication by influencing such properties as adhesion, hardness, vitrifying or glaze-forming tendency, melting or softening point, and chemical stability of the coatings. Notable among these oxides were magnetite (Fe3O4.), which had generally a beneficial influence on ceramic- to-metal adhesion, and silica (SiO2), which inhibited the oxidation of PbO and enhanced the tendency for glaze formation on the sliding surfaces. Several of the compositions studied provided protection against metal-to-metal adhesive wear, galling, or seizure at test temperatures from 750 to 1250 F. Coating friction coefficients ranged from 0.20 to 0.37 at 75 F but were around 0.08 to 0.20 at temperatures of 1250 F.