Ion and laser microprobes applied to the measurement of corrosion-produced hydrogen on a microscopic scale

摘要

An ion microprobe and a laser microprobe were used to measure concentrations of corrosion-produced hydrogen on a microscopic scale. Hydrogen concentrations of several thousand ppm were measured by both analytical techniques below the fracture surfaces of hot-salt stress-corroded titanium alloy specimens. This segregation of hydrogen below fracture surfaces supports a previously proposed theory that corrosion-produced hydrogen is responsible for hot-salt stress-corrosion embrittlement and cracking of titanium alloys. These advanced analytical techniques suggest great potential for many areas of stress-corrosion and hydrogen embrittlement research, quality control, and field inspection applications.