Failures to model the development of a cube texture during the high temperature compression of Al-Mg alloys

摘要

A strong (100) fiber texture has been observed under some circumstances after the compression and tension of Al-Mg alloys. It is not due to static recrystallization after the text, but probably connected with some form of dynamic recrystallization. Possibilities that this unusual texture might rise from some unconventional deformation mechanisms were searched for but not found.