Residual stress evolution in repair welds

摘要

The aim of this paper is to study the influence of the repair procedure on the evolution of residual stress distribution in butt welds. C-Mn steel coupon plates of 11 mm thickness were prepared, subjected to stress relief heat treatment and welded with two beads, using the gas metal arc welding process. After the deposition of two weld beads, two successive repair welds were made on the middle length of the second bead. Longitudinal and transverse residual stresses were measured in the vicinity of the weld, after deposition of the two weld beads and after each repair weld. Residual stress evaluation was conducted using an X-ray diffraction method. The repair welds caused a decrease in magnitude of the initial longitudinal residual welding stresses, and an increase of the transverse residual stress magnitude, in tension at points within the repair length, and in compression at points outside the repair length.