In-situ Processing of TiB_2 Nanoparticle-Reinforced Copper Matrix Composites

摘要

In order to produce the composite powder analyzed in this paper, two prealloys were melted and afterwards gas atomized. The obtained TiB_2-reinforced copper powder was consolidated by hot isostatic pressing (HIP). Since it is known that a decrease in the size of the reinforcing phase can cause an increase in hardness of composites, the main aim of the experimental work was to obtain as small particles of the dispersed phase as possible by using standard powder metallurgy techniques. Microstructure and microhardness of the as-cast prealloys, as-atomized powder and HIP-ed compacts were examined. The results of these examinations revealed that TiB_2 particles about 10 nm in size were in-situ formed and homogenously dispersed in the copper matrix. As a consequence of the TiB_2 formation, the microhardness of Cu-TiB_2 composite was significantly improved.