Development of input output relationships for self-healing Al_2O_3/SiC ceramic composites with Y_2O_3 additive using design of experiments

摘要

Al_2O_3/SiC ceramic composites with Y_2O_3 as an additive, was synthesized using the Taguchi method of design of experiments, so as to develop statistically sound input output relationships. The proportion of SiC was varied from 12 to 21 vol.% whereas that of Y_2O_3 was varied from 2.5 to 4 vol.%. The composites were sintered at 1500 °C for a soaking time period of 12 h in an air atmosphere. Cracks were induced on the composite surface using a Vickers indenter with a load varying between 20 and 40 kg. Fractographical analyses have been carried out using optical and/or scanning electron microscopy to investigate the surface crack propagation behavior. Thermal aging at 1300 °C in the time range of 0.5-12.5 h was applied to find optimal conditions for healing of the pre-cracked samples. The output parameters such as crack length, healed crack length, hardness and fracture toughness of the samples were correlated with appropriate inputs such as contents of SiC and Y_2O_3, crack-healing temperature, healing time, compaction pressure, indentation load using statistical analysis. Further, the extent of influence, exerted by pertinent input parameters on output parameters, was also identified.