Selective laser melting additive manufactured Inconel 718 superalloy parts: High-temperature oxidation property and its mechanisms

摘要

This work presented a comprehensive study of high-temperature oxidation behaviors and mechanisms of Selective laser melting (SLM) processed Inconel 718 superalloy parts using different methods including isothermal oxidation testing, X-ray diffraction,scanning electron microscopy and energy dispersive X-ray spectroscopy. The experimental results revealed that the oxidation process of the tested parts processed at a lower volumetric laser energy density experienced the severe spallation. On reasonably increasing the applied volumetric laser energy density, the oxidation kinetics of the as-produced parts obeyed a parabolic law, exhibiting the significantly improved oxidation resistance performance. The constitutional phases within the oxidation film were identified and the corresponding formation mechanisms were elucidated in detail according to the thermodynamic principles. The cross-sectional morphologies of oxidized Inconel 718 parts indicated that the oxidation microstructure mainly consisted of an external oxidation layer and an internal oxidation zone. The oxidation process was controlled by the outward diffusion of oxide forming elements and inward penetration of oxygen, by which the interaction mechanisms between the microstructures and internal oxidation zones were clarified. On the basis of the experimental results and theoretical analyses, the physical oxidation mechanisms were accordingly established to illustrate the oxidation behaviors of SLM-processed Inconel 718 parts at elevated operative temperatures.