Graft-Interpenetrating Polymer Networks of Epoxy with Polyurethanes Derived from Poly(ethyleneterephthalate) Waste

摘要

Polyester polyurethanes derived from poly(ethyleneterephthalate) (PET) glycolysates were blended with epoxy to form graft-interpenetrating networks (IPNs) with improved mechanical properties. Microwave-assisted glycolytic depolymerization of PET was performed in the presence of polyethylene glycols of different molecular weights (600–1500). The resultant hydroxyl terminated polyester was used for synthesis of polyurethane prepolymer which was subsequently reacted with epoxy resin to generate grafted structures. The epoxy-polyurethane blend was cured with triethylene tetramine under ambient conditions to result in graft IPNs. Blending resulted in an improvement in the mechanical properties, the extent of which was found to be dependant both on the amount as well as molecular weight of PET-based polyurethane employed. Maximum improvement was observed in epoxy blends prepared with polyurethane (PU1000) at a loading of 10 w/w which resulted in 61 increase in tensile strength and 212 increase in impact strength. The extent of toughening was quantified by flexural studies under single edge notch bending (SENB) mode. In comparison to the unmodified epoxy, the Mode I fracture toughness (K_(IC)) and fracture energy (G_(IC)) increased by ~45 and ~184, respectively. The underlying toughening mechanisms were identified by fractographic analysis, which generated evidence of rubber cavitation, microcracking, and crack path deflection.