Crystallization kinetics of amorphous nanostructured Pd_40.5Ni_40.5P_19 alloys

摘要

When a homogeneous amorphous Pd_40.5Ni_40.5P_19 alloy was subjected to thermal annealing for 30 min at various temperatures, novel microstructures were observed. At an annealing temperature of 603 K, phase separation of the amorphous phase dominated. At 628 K, a precipitation reaction proceeded first. After its completion, a eutectic growth set in. At 638 K, metastable spinodal decomposition occurred first, followed by a eutectic growth. Finally at 673 K, crystal growth of crystalline spinodal network was fast enough to compete with a eutectic growth.